Epoxy Resin Solid Cast 606 Resin Jewellery 3:1 – 4kg Kit

Kit Includes:

1 x 3kg of Part A in a 1 litre Bottle

1 x 1kg Part B in a 250ml Bottle

Epoxy Resin Solid Cast 606 Resin Jewellery 3:1 can be cast to create chess pieces or paperweights with embedded items like coins, medals, shells, brand logos, and collectibles.

Long used in industry as a capping resin over metal badges,Epoxy Resin Solid Cast 606 Resin Jewellery 3:1 has ideal surface tension and viscosity.

An superb doming resin for artwork, Solid Cast 606 | Resin Jewellery 3:1 has the ideal surface tension and viscosity.

Solid Solutions for Colour Transparent and Pigments Dyes for a consistent, opaque hue. Pour the finest hard clear resin jewellery on top of wood, artwork, metal badges, or other surfaces.

• Mixing Ratio 3:1 weight
• Working time 40min @ 25° C
• Low Viscosity
• Super Ultra Clear Finish
• Matches 50 coats of varnish

Jewellery Making ✔  Pendants ✔  Bangles ✔  Timber ✔  Earrings ✔  Necklace Making ✔ Clear Doming Resin ✔ Key Rings ✔ Medallions ✔ Food Contact Safe ✔

Temperature Resistance – up to 80 degrees Celsius

DIRECTIONS:

Mix thoroughly in a straight sided, flat bottomed container.
Using a flat ruler shaped mixing stick, mix well, scraping around the sides and base of the container. Mix until the material is crystal clear, free of any streaks.

A thin layer of resin will cure between 20 and 30°C in 24 hours. Do not let the temperature drop below 20°C. Small castings and thin layers of room temperature cured resin can prove brittle in some applications. Maximum impact strength is gained by after 5 days. A maximum block casting of around 250ml can be achieved in a silicone rubber mould.

MIX RATIO:

Measure out 3 parts A to 1 part B by weight using a scale. DO NOT MIX BY VOLUME.

PRODUCT STORAGE:
Always keep caps on bottles when not in use. Store at room temperature (18°) away from direct sunlight.
Do not store on concrete floors.

TIPS FOR USE:

Note resins and hardeners’ have a tendency to go thick and cloudy in cold weather. Check materials are clear and free flowing before using. Material can be reconstitution by standing the bottles with caps removed, in very hot water and stir the contents until the liquids are runny and non-cloudy. Allow to cool back to room temperature before proceeding with mixing.